性能项目试验条件[状态]测试方法测试数据数据单位物理性能模塑收缩率ASTM D-9550.4-0.7%比重ASTM D-7921.0423/23℃熔体流动速率200℃ 5kg(条件G)ASTM D-12384.5g/10min熔体流动速率200℃ 21.6kgASTM D-123850g/10min机械性能洛氏硬度ASTM D-785108R缺口冲击强度23℃ 1/4in(6.4mm)ASTM D-25623kg.cm/cm缺口冲击强度23℃ 1/8in(3.2mm)ASTM D-25626kg.cm/cm弯曲模量23℃ASTM D-79024000kg/cm2弯曲强度23℃ASTM D-790650kg/cm2伸长率ASTM D-63830%拉伸强度23℃ASTM D-638480kg/cm2热性能维卡软化点ASTM D-152595(203)℃(℉)热变形温度未退火6.4mm 18.6kg/cm2ASTM D-64885(185)℃(℉)退火6.4mm 18.6kg/cm2ASTM D-64895(203)℃(℉)"};